ASTM F67 Medical Titanium Rods

Baoji Ronghao Ti Co., Ltd

ASTM F67 Medical Titanium Rods

Place of Origin : Baoji

Brand Name : Ronghao Ti

Certification : IS0

MOQ : Negotiable

Price : Negotiable

Packaging Details : Standard Packing

Delivery Time : 15 days since receiving payment

Payment Terms : T/T,L/C,Western Union,Paypal and MoneyGram

Supply Ability : 20 Ton per Month

Contact Now

Titanium rods

♦ Categories: Rough Machining/Polished/Grinded/Rolled/Hot Forged/Cold Drawn/Extruded/Swaged Bar/Rod
♦ Standard: ASTM B 348, ASTM B 367, ASTM B 381, ASTM F 67, ASTM F 136, GB/T 2965, GB/T 13810
♦ Basic Grade: TAl/Grl, TA2/Gr2, TA3/Gr3, TA4/Gr4, TA5, TA6, TA7/Gr6, TA9/Gr7, TA10/Grl2, TA13,
TA15, TA19, TB2, TCI, TC2, TC3, TC4/Gr5, TC4ELI/Gr23, TC6, TC9, TC10, TC11, TC12
♦ Status: Hot Working (R), Cold Working (Y), Annealed (M), Hot Swaged (R)
♦ Diameter or Section Thickness (mm): >7-230, 5.0-8.0 {Hot Swaged Bar/Rod)
♦ Length (mm): 300-6000 (Hot Working (R), Cold Working (Y)), 300-3000 (Annealed (M)), 300-1500 (Hot Swaged (R))

Details
Forged Titanium rods: diameter (26-200)less than or equal to 4000mm
Rolled titanium rod: diameter (8-25)less than or equal to 1500mm
Production standards: ASTMB348, AMS4972, ASTM F67, ASTM F136, tolerances up to h7
Baoji Titanium Industry Co., Ltd. Ronghao titanium rod has good strength, hardness, low density, light weight, high temperature resistance, low temperature resistance, good mechanical properties, corrosion resistance is very good, non-magnetic, non-toxic, good heat transfer performance. At the same time, memory, and superconductivity. Hydrogen storage performance is outstanding. Titanium rods are widely used: navigation, aerospace, vacuum salt, the automotive industry, medical, sports, textile and paper industry, power industry, metallurgical industry, chlor-alkali industry, fertilizer industry, desalination and other industries. Life wristwatch case production, computers and spare parts production.
Chemical Composition of Titanium 8L Titanium Alloy

<^rade of titanium ^ Titanium-Alloy Electrodes & Rods

(GUrt ASTiM others)

Chemical Composition FractionV%
Element Residuals, Max
■Xi C o N H Fe A1 V Pd Ru Ni Mo Ce Zr Nb Co
AWS Classification IONS Number
ERTi-1 K50100 Balance 0.02 0.02-0.10 0.012 0.005 0.08
ERTi-2 k120 Balance o.oi 0.08-0.16 0.015 0.008 0.12
i-3 K50125 Balauoe 0.02 o.n-o.20 0.02 0.16
EJifi-4 k130 Balauoe 0.02 0.18-0-i2 0.025 0.25
EJifi-5 K56402 Balauoe 0.05 0.12-0.20 0.02 0.015 0.22 5.S-6.75 15-4.5
i-7 K52401 Balauoe 0.02 0.08-0. If; 0.015 0.12 0.12-0.25
ERtiER1i-$ELI K56321 Balauoe 0.02 0.06-0.12 0.012 0.005 02 2.5-15 2.0-2.0
ERH-11 R52251 Balauoe 0.02 0.02-0.10 0.012 0.005 0.0S 0.12-0.25
ERH-12 K53401 Balauoe 0.02 0.08-0. If; 0.015 0.05 0.6-0.9 0.2-0.4
ERH-13 K53423 Balauoe 0.02 0.02-0.10 0.012 0.005 0.0S 0.04-0.06 0.4-0 .£;
ERH-14 R53424 Balauoe 0.02 0.08-0. If; 0.015 0.12 0.04-0.06 0.4-0 .£;
ER11-15A K53416 Balauoe 0.02 0.12-0.20 0.02 0.16 0.04-0.06 0.4-0 .£;
K52403 Balauoe 0.02 0.08-0. If; 0.015 0.12 0.04-0.08
ERTi-17 K52253 Balauoe 0.02 0.02-0.10 0.012 0.005 0.0S 0.04-0.08
ERH-1S K56326 Balauoe 0.02 0.06-0.12 0.012 0.005 0.20 2.5-15 2.0-2.0 0.04-0.08
ERH-1!) K641 Balauoe 0.02 0.06-0.10 0.015 0.015 0.20 2.0-4.0 7.S-S.S 2.S-4.5 S.S-6.S 15-4.5
ERH-20 K6 Balauoe 0.02 0.06-0.10 0.015 0.015 0.20 2.0-4.0 7.S-S.S 0.04-0.08 2.S-4.5 S.S-6.S 15-4.5
ERH-21 K5S2U Balauoe 0.02 0.10-0.15 0.012 0.005 0.20-0.40 2.5-15 14.0-16.0 2.2-12 0.15-0.25
ERH-23 K5640S Balauoe 0.02 0.02-0.11 0.012 0.005 0.20 S.S-6.S 15-4.5
ERH-24 R56415 Balauoe 0.05 0.12-0.20 0.02 0.015 0.22 5.S-6.75 15-4.5 0.04-0.08
ERH-25 R5640 Balauoe 0.05 0.12-0.20 0.02 0.015 0.22 5.S-6.75 15-4.5 0.04-0.08 0.2-0.S
R52405 Balauoe 0.02 0.08-0. If; 0.015 0.12 0.08-0.14
ERTi-27 R5225S Balauoe 0.02 0.02-0.10 0.012 0.005 0.0S 0.08-0.14
ERH-2S R56324 Balauoe 0.02 0.06-0.12 0.012 0.005 0.20 2.5-15 2.0-2.0 0.08-0.14
ERH-2!) R56414 Balauoe 0.02 0.02-0.11 0.012 0.005 0.20 S.S-6.S 15-4.5 0.08-0.14
ERH-30 R53531 Balauoe 0.02 0.08-0. If; 0.015 0.12 0.04-0.08 020-0.SO
ERH-31 R53533 Balauoe 0.02 0.12-0.20 0.02 0.16 0.04-0.08 020-0.SO
ERH-32 R55112 Balauoe 0.02 0.05-0.10 0.012 0.20 4.5-5.5 0.6-1.4 0.6-12 0.6-1 A 0.06-0.14 0.6-1 A
ERH-33 R53443 Balauoe 0.02 0.08-0. If: 0.015 0.12 0.01-0.02 0.02-0.04 O^S-O.55 0.1-0.2
ERH-34 R53444 Balauoe 0.02 0.12-0.20 0.02 0.16 0.01-0.02 0.02-0.04 O^S-O.55 0.1-0.2
ERll-36 451 Balauoe 0.02 0.06-0.12 0.02 0.0025 0.02 42.0-47.0
ERH-3S R52451 Balauoe 0.05 0.20-0.27 0.02 0.010 1.2-1.S 2.5-4.S 2.0-2.0
Chemical Composition (Mass Fraction)/%

Grade of "Titanium Alloy 〇4p alloy

{GByl1 ASTM others)

Nominal Element Impurity {Max.)
Chemical ComposLtion 1i Al &i Mo Cr Mn Cu Si Fe N H Residuals, Max.
£adi total
"TCI Orr‘1 Ti-2Al-1.5MD Balanoe 1.0~2.5 0.7~2.0 0.20 0.08 0.05 0.012 0.15 0.10 0.40
1C2 cm Ti-4Al-1.5MD Ealaiioe i. 5-5.0 0.8-2.0 0.20 0.08 0.05 0.012 0.15 0.10 0.40
tC3 Ti-5A1-4V Ealaiioe 4.5-6.0 2.5-4.5 0.20 0.08 0.05 0.015 0.15 0.10 0.40
1C4 Gr5 R45400 Ti-6A1-4V Ealaiioe 5.5-6.75 2.5-4.5 CV: 0.005) 0.20 0.08 0.05 0.015 0.20 0.10 0.40
tC4ELI GrSELI R56407 Q^23 Ti-fiAl^tVEU Ealaiioe 5.5-6.5 2.5-4.5 CV: 0.005) 0.25 0.08 O.ftJ 0.012 0.12 0.10 0.30
tC6 Bt3-1 Ti-6 Al-1.5Cr-2.5M〇-0. SFc^O 3Si Eslauoe 5.5-7.0 2.0-2.0 0.8-2.2 0.1S-0.40 0.2-0.7 0.08 0.05 0.015 0.18 0.10 0.40
tCS M'S Ti-6.5Al-2.5M^025Si Ealaiioe 5.8-6.8 2.S-2.8 0.20-0.25 0.40 0.08 0.05 0.015 0.15 0.10 0.40
Ti-6.5A1-2 .SU^2,5Sn-0 .iSi Ealaiioe 5.8-6.8 1.8-2.8 2.S-2.8 0.20-0.40 0.40 0.08 0.05 0.015 0.15 0.10 0.40
1C10 R5<62〇 H-662 Ti-6Al-6V-2Sn Ealaiioe 5.5-6.5 1.5-2.5 5.5-6.5 0.25-1.0 0.25-1.00 0.08 0.04 0.015 0.20 0.10 0.40

Grade of "TitBrnum Alloy 〇4p alloy

(GB/l1 AS1M others)

Nominal

Chemical Composition

Chemical Composition (Mass Fraction)/%
Element Impurity {Max.)
1i Al &i Mo V Cr Zr Nb Si Fe C N H o Residuals, Max.
£adi total
icii Ti-6.5 Al-2.5fcfo-1.52i--0.2Si Eslauoe 5.8-7.0 2.S-2.8 0.8-2.0 0.2-0.25 0.25 0.08 0.05 0.012 0.15 0.10 0.40
1C12 Ti- 5Al-4MD-4〇r-22r-2Sn- lNb Ealaiioe 4.5-5.5 1.5-2.5 2.S-4.S 15-4.5 1.5-10 0.5~1.5 0.20 0.08 0.05 0.015 0.20 0.10 0.40
1C15 Ti-5Al-2.5Fe Ealaiioe 4.5-5.5 2.0-2.0 0.08 0.05 0.012 0.20 0.10 0.40
tci6 m6 Ti-2A1-5M^4.5V Ealaiioe 2.2-18 4.S-5.S 4.0-5.0 名 0.15 0.25 0.08 0.05 0.012 0.15 0.10 0.30
1C17 R52252 ^i-17 Ti-5Al-2Sn-22r-4Mo-4Cr Eslauoe 4.S-.5 1_5~2_5 2.S-4.S 1.5-2.5 0.25 0.05 0.05 0.0125 0.08-0.12 0.10 0.30
1C1S M-22 Ti- 5 Al-4,75Mo-4.7 5 V-1 Cr-1 Fe Ealaiioe 4.4~5.7 4.0-5.5 4.0-5.5 0.5-1. S ^0.20 名 0.15 O.S-1.5 0.08 0.05 0.015 0.18 0.10 0.30
1C19 R5<2<0 fi-6246 Ti-6Al-2Sn-42r-6Mo Ealaiioe 5.5-6.5 1.75-2.25 5.5-6.5 15-4.5 0.15 0.04 0.04 0.0125 0.15 0.10 0.40
tC2〇 R5<700 1MI3<7 Ti-6Al-7Nb Ealaiioe 5.5-6.5 6.5^75 Ta ^0.5 0.25 0.08 0.05 0.009 0.20 0.10 0.40
1C21 {CH-62222S) Ti-6Al-2fcfo-1.5Cr-22r-2Su-2Nb Eslauoe 5.2-6.8 1.6-2.5 2.2-23 0.9-2.0 1.6-2.5 1.7-23 0.15 0.08 0.05 0.015 0.15 0.10 0.40
t〇22 Gr24 Ti-6Al-4 V-0 ,〇5Pd {Ti-6 A1-4VSTA) Ealaiioe 5.5-6.75 2.5-4.5 CV: 0.005) Pd: 0.04-0.08 0.40(0.20) 0.08 0.05 0.015(0.0125) 0.20 0.10 0.40
1C23 Gr29 R56404 Ti-6Al-4V-0.lRu Ealaiioe 5.5-6.75 2.5-4.5 Ru: 0.08-0.14 0.25 0.08 0.05 0.015 0.12 0.10 0.40
1C24 1i-4322 SP-700 Ti-4.5Al-2V-2Mo-2Fe Ealaiioe 4.0-5.0 l.S-22 2.5~15 1.7-2.3 0.05 0.05 0.010 0.15 0.10 0.40
1C25 M-25 Ti-6.5 Al-2Mo-l 2r-1 Sd- 1 W-0.2Si Ealaiioe 6.2~7.2 0.8-2.5 1.S-2.S W: 0.5-1.5 0.8-2.5 0.10-0.25 0.15 0.10 0.04 0.012 0.15 0.10 0.30
tCZ6 Ti-l2NM22r Ealaiioe 12.5-14.0 12.5-14.0 0.25 0.08 0.05 0.012 0.15 0.10 0.40
Grade of Titanium Alloy {GBAf A^M odiers)

Nominal

Chemical Composition

Chemical Comp<xsLfion{Mass JVacfion)/%
Element Impurity (Max.)
1i A1 Mo V Mn Zr Si Nd Fe C N H o Residuals, Max.
Each total
TA20 (CITT-2) Ti-4Al-2V-1.52r Balance i.S-4.5 2.5-15 l.ft-2.0 0.10 0.15 0.05 0.04 0.002 0.12 0.10 0.30
TA21 {0t4-0) Ti-lAl-lMn Balaircc 0.4-1.5 0.S-1.2 ^020 0.12 0.30 0.10 0.05 0.012 0.15 0.10 0.20
1A22 CIi-31) Ti-2Al-lMo-lNi-l2r Balaircc 2.S-2.5 0.5-1.5 Ni: 03-1.0 0.8-2.0 0.15 0.20 0.10 0.05 0.015 0.15 0.10 0.20
TA22-1 C^IA) Ti-2Al-lMo-lNi-l2r Balaircc 2.S-2.5 0.2-0.8 Ni: 03-0.8 0.S-1.0 0.04 0.20 0.10 0.04 0.008 0.10 0.10 0.20
1A23 CH-70) Ti-2.5Al-22r-lFe Balaircc 2.2-2.0 Ni: 0.8-1.2 1.7-2.2 0.15 0.10 0.04 0.010 0.15 0.10 0.20
TA23-1 C^-7〇A) Ti-2.5Al-22r-lFe Balaircc 2.2-2.0 Ni: 0.8-1.1 1.7-2.2 0.10 0.10 0.04 0.008 0.10 0.10 0.20
1A24 CIi-75) Ti-iAl-2fcfo-22r Balaircc 2.S-2.5 1.0-2.5 1.0-2.0 0.15 0.30 0.10 0.05 0.015 0.15 0.10 0.20
1A24-1 C^-^SA) Ti-iAl-2fcfo-22r Balaircc l.S-2.5 1.0-2.0 1.0-2.0 0.04 0.15 0.10 0.04 0.010 0.10 0.10 0.20
tA25 GrlS Ti-iAl-2.5V-0.05f>d Balaircc 2.S-2.5 2.0-10 M 0.04-0.08 0.25 0.08 O.ftJ 0.015 0.15 0.10 0.40
tA26 Gr25 R56323 Ti-iAl-2.5V-0.lRu Balaircc 2.S-2.5 2.0-10 Ru: 0.0S-0.14 0.25 0.08 O.ftJ 0.015 0.15 0.10 0.40
1A27 Gr2-6 R52404 Ti-0.10Ru Balaircc Ru: 0.08-0.14 0.20 0.08 O.ftJ 0.015 0.25 0.10 0.40
1A27-1 Gr27 Ti-0.10Ru Balaircc Ru: 0.08-0.14 0.20 0.08 O.ftJ 0.015 0.18 0.10 0.40
1A2S Ti-iAl Balaircc 2.0-2.0 0.30 0.08 O.ftJ 0.015 0.15 0.10 0.40

Grade of Titanium Alloy p alloy

{GBflf ASTMo^icrs)

Nominal

Chemical Compixsition

Chemical Comp<xsifion(M3ss fVacfioii)/%
Element Impurity ^rfax.)
ti A1 &i Mo V Cr 2r Pd Fe C N H o Residuals, Max.
£acb total
r〇2 Ti-5Mo-5V-80r-2Al Balaircc 2.S-2.5 4.7~5.7 4.7-S.7 7.S-8.5 0.30 0.05 0.04 0.015 0.15 0.10 0.40
m3 Ti-l5Al-10fcfo-SfV-lFe Balaircc 2.7~i.7 9.5-11.0 7.S-8.5 0.8-12 0.05 0.04 0.015 0.15 0.10 0.40
1B4 Ti-4Al-7M^10V-2F^l2r Balaircc 2.0-4.5 0-7.8 9.0-10.5 O.S-1.5 1_5~2_S 0.05 0.04 0.015 0.20 0.10 0.40
Ti-15-3-3-3 Ti-15V-2Al-iCr-2Sii Balaircc 2.S-2.5 2.S-2.5 14.0-16.0 2.S-2.5 0.25 0.05 0.05 0.015 0.15 0.10 0.20
^6 R56410 1i-l〇23 Ti-10V-2F^2Al Balaircc 2.6-2.4 9.0-11.0 (Y: 0.005) 1.6-2.22 0.05 0.05 0.015 0.1 12) 0.10 0.20
tB7 H-32 Ti-22Mo Balaircc 20.0-24.0 0.30 0.05 0.05 0.015 0.20 0.10 0.40
|!21s Ti-15M^2Al-2.7N^0.2SSi Balaircc 2.S-2.5 14.0-16.0 Nb: 2.4-12 Si: 0.1S-0.25 0.40 0.05 0.05 0.015 0.17 0.10 0.40
R5S640 pc Ti-iAl-8V-6Cr-4Mo^2r Balaircc 2.0-4.0 2.5-4.5 7.S-8.5 5.S-6.5 2.S-4.5 名 0.10 0.30 0.05 O.ftJ O.ftJO 0.14 0.10 0.40
1U10 CHJ523) Ti-5Mo-5V-2Cr-2Al Balaircc 2.S-2.5 4.5~5.5 4.S-5.5 l.S-2.5 0.30 0.05 0.04 0.015 0.15 0.10 0.40
tBll Ti-15Mo Ti-l5Mo Balaircc 14.0-16.0 0.10 0.10 0.05 0.015 0.20 0.10 0.40

Grade of Yitamum

CP Titanium & a alloy {GB/Tf ASTTM IONS others)

Nominal

Chemical Composition

Chemical Composition (Mass JVactLon)/%
Element Impurity
ti A1 Mo Pd Ni Si C Fe C N H o Residuals, Max.
£adb Total
tAl£LI CrlEO CP Titanium Balacrcc 0.10 o.fti 0.012 0.008 0.10 0.05 0.20
1A1 Grl R5ft25〇 Ml-00 CP Titanium Balazrce 0.20 0.08 O.ftJ 0.015 0.18 0.10 0.40
tAl-1 Bfl-OOCB CP Titanium Balance 名 0.20 ^0.08 0.15 0.05 O.ftJ 0.002 0.12 0.10
TA2ELI Gr2ELI CP Titanium Balaircc 0.20 0.05 O.ftJ 0.008 0.10 0.05 0.20
1A2 Gr2 R50400 1^2 CP Titanium Balaircc 0.30 0.08 O.ftJ 0.015 0.25 0.10 0.40
TA3ELI Gr3ELI CP Titanium Balaircc 0.25 0.05 0.04 0.008 0.18 0.05 0.20
1A3 Gr3 K50550 CP Titanium Balaircc 0.30 0.08 0.05 0.015 0.25 0.10 0.40
TA4ELI Gr4ELI CP Titanium Balaircc 0.30 0.05 0.05 0.008 0.25 0.05 0.20
1A4 Gr4 R50700 CP Titanium Balaircc 0.50 0.08 0.05 0.015 0.40 0.10 0.40
1A5 Ti-4A1-0.005B Balaircc 2.>4.7 0.005 0.20 0.08 0.04 0.015 0.15 0.10 0.40
TAi BTf5 Ti-5A1 Balaircc 4.0-5.5 0.30 0.08 0.05 0.015 0.15 0.10 0.40
TA7 Gr6 R54520 BT5-1 Ti-5Al-2.SSn Balaircc 4.0-6.0 2.0-2.0 0.50 0.08 0.05 0.015 0.20 0.10 0.40
TA7ELICIA70) R54521 Ti-5Al-2.5SnEn Balaircc 4.50-5.75 2.0-2.0 0.25 0.05 0.025 0.0125 0.12 0.05 0.30
tAS Qrl6 R52402 Ti-0.05f>d Balaircc 0.04-0.08 0.30 0.08 O.ftJ 0.015 0.25 0.10 0.40
tAS-1 Grl7 R52252 Ti-0.05f>d Balaircc 0.04-0.08 0.20 0.08 O.ftJ 0.015 0.18 0.10 0.40
1A$ Gr7 R52400 Ti^.2Pd Balaircc 0.12-0.25 0.30 0.08 O.ftJ 0.015 0.25 0.10 0.40
TA9-1 Grll R52250 Ti^.2Pd Balaircc 0.12-0.25 0.20 0.08 O.ftJ 0.015 0.18 0.10 0.40
TA10 Grl2 R53400 Ti-03M^0.8Ni Balaircc 02-0.4 0.6-0.9 0.30 0.08 O.ftJ 0.015 0.25 0.10 0.40
Grade of *Htamuin {GBflf A^fMovers)

Nominal

Chemical Compixsition

Chemical ComjHxsifion (Mass ¥Vaction)/0/〇
Element Impurity
ti A1 &i Mo V 2r Si Nd Fe C N H o Residuals, Max.
£acb total
TAll K54S10 Ti^ll Ti-8Al-lfcfo-lV Balaircc 7.25-8.35 0.75-1.25 0.7S-1.25 0.30 0.08 0.05 0.015 0.12 0.10 0.30
TA12 {Tfi-Sll) Ti-5.5A1-4Sd-22t- 1Mo-1 Nd-0,25Si Balaircc 4.S-6.0 17-4.7 0.75-1.25 l.S-2.5 0.2-0.25 0.6-1.2 0.25 0.08 0.05 0.0125 0.15 0.10 0.40
TA12-1 cn^sn) Ti-5.5A1-4Sd-22t- 1Mo-1 Nd-0,25Si Balaircc 4.S-5.5 17-4.7 1.0-2.0 l.S-2.5 0.2-0.25 0.6-1.2 0.25 0.08 0.04 0.0125 0.15 0.10 0.30
tAB IMI230 Ti-2.5Cu Balaircc Cu: 2.0-2.0 0.20 0.08 0.05 0.010 0.20 0.10 0.30
tA14 H-679 Ti-2.2 Al-11 So- SZx- IMo-0 ,2Si Balaircc 2.ft-2.5 10.52-11.5 03-1.2 4.0-6.0 0.10-0.50 0.20 0.08 0.05 0.0125 0.20 0.10 0.30
1A1S CT2〇 Ti-6.5Al-lM^lV-22r Balaircc S.S-7.1 0.5-2.0 0.&-2.5 l.S-2.5 0.15 0.25 0.08 0.05 0.015 0.15 0.10 0.30
tA15-l I«f20-1CB Ti-2.5Al-lM^lV-l.S2r Balaircc 2.0-2.0 0.5-1. S O.S-1.5 1.0-2.0 0.10 0.15 0.05 0.04 0.002 0.12 0.10 0.30
TA15-2 l«f2〇-2CB Ti-4Al-lhfo-lV-1.52r Balaircc 2.S-4.5 0.5-1. S O.S-1.5 1.0-2.0 0.10 0.15 0.05 0.04 0.002 0.12 0.10 0.30
TA16 ilH-TM) Ti-2Al-2.52i Balance 1.8-2.5 2.0-10 0.12 0.25 0.08 0.04 0.006 0.15 0.10 0.30
1A17 {MtoB) Ti-4A1-2V Balaircc 2.S-4.5 1.5-2.0 0.15 0.25 0.08 0.05 0.015 0.15 0.10 0.30
tAlS Orif R5<632〇 0t4-lB Ti-2A1-2.5V Balaircc 2.0-2.5 1.5-2.0 0.25 0.08 0.05 0.015 0.12 0.10 0.30
TA19 R5462-0 •H-6242S Ti-6Al-2Sn^2r-2fcfo Balaircc 5.5-6.5 1.&-2.2 1.8-2.2 CV: 0.005) l.^A.4 Si: ^0.12(0.06-0.1) 0.25 0.05 0.05 0.015 0.15(0.12) 0.10 0.30

Product Tags:

ASTM F67 Medical Titanium Rods

      

AMS4972 Medical Titanium Rods

      

25mm Titanium Bar

      
Buy cheap ASTM F67 Medical Titanium Rods product

ASTM F67 Medical Titanium Rods Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Baoji Ronghao Ti Co., Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)